Título: | Pulsed direct current magnetron sputtered nanocrystalline tin oxide films | Autor: | Reddy, A. Sivasankar Figueiredo, N. M. Cavaleiro, A. |
Palavras-chave: | Oxides; Thin films; Sputtering; Electrical; Optical | Data: | Set-2012 | Editora: | Elsevier | Citação: | REDDY, A. Sivasankar; FIGUEIREDO, N. M.; CAVALEIRO, A. - Pulsed direct current magnetron sputtered nanocrystalline tin oxide films. "Applied Surface Science". ISSN 0169-4332.258:22 (2012) 8902-8907 | Título da revista, periódico, livro ou evento: | Applied Surface Science | Volume: | 258 | Número: | 22 | Resumo: | The nanocrystalline tin oxide (SnO2) films were deposited on glass substrates by pulsed magnetron sputtering technique and subsequently annealed from 200 to 500 °C. The structural, microstructural, electrical, and optical properties of as deposited and annealed SnO2 films were studied. The crystallinity degree of the films increased with annealing temperature. Photoluminescence (PL) measurements showed that the emission peaks have low intensity and are positioned at 535 nm (2.31 eV) and 605 nm (2.05 eV) in as deposited SnO2 films. The intensity of PL peak increases sharply with the increasing of annealing temperature. The as deposited films exhibited high electrical resistivity and low optical transmittance. After annealing at 500 °C, the electrical resistivity of the films decreased to the lowest value of 0.015 Ω cm, being the optical transmittance 90%. | URI: | https://hdl.handle.net/10316/24817 | ISSN: | 0169-4332 | DOI: | 10.1016/j.apsusc.2012.05.112 | Direitos: | openAccess |
Aparece nas coleções: | I&D CEMMPRE - Artigos em Revistas Internacionais FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Pulsed direct current magnetron sputtered.pdf | 579.7 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
17
Visto em 7/out/2024
Citações WEB OF SCIENCETM
5
13
Visto em 2/out/2024
Visualizações de página
330
Visto em 15/out/2024
Downloads 50
416
Visto em 15/out/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.