Título: | Influence of temperature processing on the microstructure and hardness of the 420 stainless steel produced by hot pressing | Autor: | Cunha, A. Marques, A. Gasik, M. Trindade, B. |
Palavras-chave: | 420 stainless steel; hot pressing; microstructure; grain size; microhardness | Data: | 2022 | Editora: | Taylor & Francis | Projeto: | SFRH/BD/147460/2019 UIDB/04436/2020 UIDP/04436/2020 UIDB/00285/2020 |
Título da revista, periódico, livro ou evento: | Materials and Manufacturing Processes | Volume: | 38 | Número: | 3 | Resumo: | In this study, samples of 420 stainless steel were obtained by hot pressing from powder at temperatures from 1,100 to 1,200°C. The aim was to explore the influence of the processing temperature on their grain size, microstructure, densification and mechanical properties. The results showed that it is possible to produce dense samples at these sintering temperatures. The sintering temperature influenced the density, grain size, structural phases, and hardness of the samples. Martensite and austenite were present in the samples sintered at 1,100, 1,150, and 1,180°C. Precipitation of Cr23C6 was observed after sintering at 1,200°C. This sample was the one with the highest density (99.7% densification) and hardness (771.9 HV). | URI: | https://hdl.handle.net/10316/115001 | ISSN: | 1042-6914 1532-2475 |
DOI: | 10.1080/10426914.2022.2072885 | Direitos: | openAccess |
Aparece nas coleções: | I&D CEMMPRE - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Influence-of-temperature-processing-on-the-microstructure-and-hardness-of-the-420-stainless-steel-produced-by-hot-pressingMaterials-and-Manufacturing-Processes.pdf | 2.91 MB | Adobe PDF | Ver/Abrir |
Visualizações de página
38
Visto em 28/ago/2024
Downloads
29
Visto em 28/ago/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.