Title: Resistência mecânica do betão curado em condições adiabáticas
Other Titles: Mechanical resistance of concrete cured in adiabatic conditions
Authors: Duarte, Diogo Martins
Orientador: Lopes, Adelino Vasconcelos
Lopes, Sérgio Manuel Rodrigues
Keywords: betão; temperatura de cura; resistência à compressão; propriedades térmicas; concrete; curing temperature; compressive strength; thermal properties
Issue Date: 7-Sep-2018
Serial title, monograph or event: Resistência mecânica do betão curado em condições adiabáticas
Place of publication or event: DEC-FCTUC
Abstract: As grandes estruturas de betão, tais como as barragens, as pontes, etc, apresentam um elevado potencial para fissurar, em resultado de tensões induzidas por gradientes de temperatura gerados no interior do betão. Estes gradientes de temperatura ocorrem quando o calor gerado no betão é dissipado para o meio envolvente. Nestas condições, a temperatura na superfície do betão é inferior à verificada no interior; daí as tensões de tração no betão superficial. Como este fenómeno se verifica no início do endurecimento do betão, é fácil as tensões de tração serem superiores à sua resistência à tração, provocando fissuras, que em última instância afetam a integridade e a durabilidade da estrutura. Trabalhos existem onde se estudaram as questões térmicas. Conhece-se relativamente bem o poder calorífico e o coeficiente de transmissibilidade destes materiais enquanto maciços infinitos. Mas não se conhece com o devido rigor quais as consequências da temperatura de cura na resistência destes materiais.Na presente dissertação pretende-se avaliar as alterações das propriedades resistentes de um betão sujeito a diferentes temperaturas de cura. Para o efeito, serão construídos diversos cubos, curados a diversas temperaturas, onde se tentará compreender a evolução da resistência ao longo do tempo. Relativamente às temperaturas de cura, a análise será iniciada colocando os provetes em condições ambientais, e depois em ambiente controlado, usando uma estufa para o efeito..........................
Large concrete structures, such as dams and bridges, have a high potential for cracking due to tensions induced by temperature gradients generated inside the concrete. These temperature gradients occur when heat generated in the concrete is dissipated into the surrounding environment. In these conditions, the concrete surface temperature is lower then one observed in the interior; hence the tensile stresses in the surface concrete. Since this phenomenon occurs at the beginning of concrete hardening, it is easy for tensile stresses to exceed the concrete tensile strength, causing cracks, which ultimately affect the integrity and durability of the structure.Works exist where the thermal issues were studied. The calorific value and the coefficient of transmissibility of these materials as infinite masses are known relatively well. But the consequences of the curing temperature on the strength of these materials are not known with due rigor.In the present dissertation it is intended to evaluate the changes of the resistant properties of a concrete subject to different curing temperatures. For this purpose, several cubes cured at different temperatures will be built, where an attempt will be made to understand the evolution of the resistance over time. Regarding the curing temperatures, the analysis will begin by placing the test specimens under ambient conditions and then in a controlled environment using a greenhouse for this purpose..............................................
Description: Dissertação de Mestrado Integrado em Engenharia Civil apresentada à Faculdade de Ciências e Tecnologia
URI: http://hdl.handle.net/10316/87288
Rights: openAccess
Appears in Collections:UC - Dissertações de Mestrado

Files in This Item:
File Description SizeFormat
Resistência mecânica do betão curado em condições adiabáticas.pdf3 MBAdobe PDFView/Open
Show full item record

Page view(s)

180
checked on Apr 1, 2020

Download(s)

174
checked on Apr 1, 2020

Google ScholarTM

Check


This item is licensed under a Creative Commons License Creative Commons