Título: | Influência do teor de grafite exfoliada nas propriedades do polipropileno isotático | Outros títulos: | Influence of exfoliated graphite content on the properties of isotatic polypropylene | Autor: | Carvalho, Ana Rita Malheiro da Silva | Orientador: | Vieira, Maria Teresa Freire | Palavras-chave: | Grafeno Multicamadas; Grafite; Polipropileno; Nanocompósito; Graphene multilayers; Graphite; Polypropylene; Nanocomposites | Data: | 29-Set-2017 | Título da revista, periódico, livro ou evento: | Influência do teor de grafite exfoliada nas propriedades do polipropileno isotático | Local de edição ou do evento: | Departamento de Engenharia Mecânica | Resumo: | O principal objetivo deste trabalho é avaliar a viabilidade da incorporação de grafite recuperada de elétrodos em fim de vida provenientes da industria metalomecânica numa matriz de polipropileno, face à adição de grafeno multicamadas comercial. O polipropileno foi escolhido como material base pelo facto de ser um dos polímeros mais comercializados, cujo o seu processamento é fácil e apresenta uma reciclabilidade muito alta. Os nanocompósitos foram produzidos por um processo de fusão e a sua caracterização foi realizada a partir da injeção de provetes. O foco deste trabalho foi a caracterização das propriedades mecânicas com a realização de ensaio de tração e flexão em três pontos. Foram analisados reforços com cargas de 0.5%wt e 1%wt de grafite recuperada e grafeno multicamadas.O principal objetivo deste trabalho é avaliar a viabilidade da incorporação de grafite recuperada de elétrodos em fim de vida provenientes da industria metalomecânica numa matriz de polipropileno, face à adição de grafeno multicamadas comercial. O polipropileno foi escolhido como material base pelo facto de ser um dos polímeros mais comercializados, cujo o seu processamento é fácil e apresenta uma reciclabilidade muito alta. Os nanocompósitos foram produzidos por um processo de fusão e a sua caracterização foi realizada a partir da injeção de provetes. O foco deste trabalho foi a caracterização das propriedades mecânicas com a realização de ensaio de tração e flexão em três pontos. Foram analisados reforços com cargas de 0.5%wt e 1%wt de grafite recuperada e grafeno multicamadas. The main objective of this work is to evaluate the feasibility of the incorporation of graphite recovered from end - of - life electrodes from the metal - mechanical industry into a polypropylene matrix, in addition to the addition of commercial multilayer graphene.Polypropylene has been chosen as the base material in that it is one of the most commercially available polymers whose processing is easy and has a very high recyclability.The nanocomposites were produced by a fusion process and their characterization was performed from the injection of test pieces. The focus of this work was the characterization of the mechanical properties with the accomplishment of test of traction and flexion in three points. Reinforcements with loads of 0.5% wt and 1% wt of recovered graphite and multilayer graphene were analyzed. The main objective of this work is to evaluate the feasibility of the incorporation of graphite recovered from end - of - life electrodes from the metal - mechanical industry into a polypropylene matrix, in addition to the addition of commercial multilayer graphene.Polypropylene has been chosen as the base material in that it is one of the most commercially available polymers whose processing is easy and has a very high recyclability.The nanocomposites were produced by a fusion process and their characterization was performed from the injection of test pieces. The focus of this work was the characterization of the mechanical properties with the accomplishment of test of traction and flexion in three points. Reinforcements with loads of 0.5% wt and 1% wt of recovered graphite and multilayer graphene were analyzed. |
Descrição: | Dissertação de Mestrado Integrado em Engenharia do Ambiente apresentada à Faculdade de Ciências e Tecnologia | URI: | https://hdl.handle.net/10316/83196 | Direitos: | closedAccess |
Aparece nas coleções: | UC - Dissertações de Mestrado |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | Entrar |
---|---|---|---|---|
Ana Rita Carvalho - Final.pdf | 2.3 MB | Adobe PDF | Pedir uma cópia |
Visualizações de página 50
439
Visto em 30/abr/2024
Downloads 50
365
Visto em 30/abr/2024
Google ScholarTM
Verificar
Este registo está protegido por Licença Creative Commons