Título: | Microstructure dependent fatigue crack growth in aged hardened aluminium alloys | Autor: | Borrego, L. P. Costa, J. M. Silva, S. Ferreira, J. M. |
Palavras-chave: | Aluminium alloys; Fatigue crack growth; Retardation; Microstructure; Crack closure; Overloads | Data: | 2004 | Citação: | International Journal of Fatigue. 26:12 (2004) 1321-1331 | Resumo: | Fatigue crack propagation tests in constant amplitude loading, as well as with single peak overloads, have been performed in AlMgSi1-T6 aluminium alloys with different Mn and Cr contents. Crack closure was monitored in all tests by the compliance technique using a pin microgauge. A moderate stress ratio and a strong material dependence effects on the fatigue crack growth were observed. These effects are discussed in terms of the different dominant closure mechanism (plasticity-induced closure or roughness-induced closure). Roughness-induced closure dominates crack closure in the alloys with higher contents of Mn and Cr elements. In the alloy with a lower content of these elements, plasticity-induced closure is dominant. When roughness-induced closure is the prime pre-overload closure mechanism, the retardation effect is decreased in comparison to when plasticity-induced closure is dominant. | URI: | https://hdl.handle.net/10316/4249 | DOI: | 10.1016/j.ijfatigue.2004.04.004 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
file848a8de7e07448f9a05932e08bfa39fe.pdf | 571.71 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
53
Visto em 7/out/2024
Citações WEB OF SCIENCETM
43
Visto em 2/out/2024
Visualizações de página 10
901
Visto em 15/out/2024
Downloads 50
499
Visto em 15/out/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.