Título: | Fe2O3/aluminum thermite reaction intermediate and final products characterization | Autor: | Durães, Luísa Costa, Benilde F. O. Santos, Regina Correia, António Campos, José Portugal, António |
Palavras-chave: | Thermite; Iron oxide/aluminum reaction; Products characterization; X-ray diffraction; Mössbauer spectroscopy; Reaction mechanism | Data: | 2007 | Citação: | Materials Science and Engineering: A. 465:1-2 (2007) 199-210 | Resumo: | Radial combustion experiments on Fe2O3/aluminum thermite thin circular samples were conducted. A stoichiometric (Fe2O3 + 2Al) and four over aluminized mixtures were tested. The combustion products were characterized by X-ray diffraction and Mössbauer spectroscopy and the influence of Fe2O3/aluminum ratio on their composition was assessed. The main products were identified as alumina ([alpha]-Al2O3) and iron (Fe). A significant amount of hercynite (FeAl2O4) was detected, decreasing with the aluminum excess in the reactants. Close to the sample/confinement interface, where reaction quenching occurs, a non-stoichiometric alumina (Al2.667O4) was observed, being its XRD intensity correlated to the hercynite amount. Fe3Al intermetallic phase was found in the products of over aluminized mixtures. A reaction mechanism was proposed comprising: (i) Fe2O3 reduction to Fe3O4 and FeO; (ii) Al oxidation to Al2O3; (iii) interaction of the remaining Al with Fe3O4 and FeO with formation of iron-aluminates (hercynite) and iron; (iv) for the over aluminized mixtures, incorporation of Al into the iron-aluminates takes place with the formation of iron and alumina and, in parallel, Al reacts with iron to produce intermetallics. | URI: | https://hdl.handle.net/10316/3786 | DOI: | 10.1016/j.msea.2007.03.063 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Química - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
filec5d47aee56004f78bda04ac1045d3b65.pdf | 1.01 MB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
127
Visto em 7/out/2024
Citações WEB OF SCIENCETM
113
Visto em 2/out/2024
Visualizações de página 20
736
Visto em 15/out/2024
Downloads 20
1.483
Visto em 15/out/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.