Título: | Increase of the filler content by using a silica-coated PCC filler | Autor: | Lourenço, A. F. Gamelas, J. A. F. Ferreira, Paulo J. |
Palavras-chave: | Calcium carbonate; Silica; Paper filler; Strength properties | Data: | 2014 | Editora: | Mid Sweden University | Citação: | LOURENÇO, A.F.; GAMELAS, J.A.F.; FERREIRA, P.J. – Increase of the filler content by using a silica-coated PCC filler. "Nordic Pulp & Paper Research Journal. 29:2 (2014), 242-247. Disponível na Internet em:<http://hdl.handle.net/10316/28277>. | Título da revista, periódico, livro ou evento: | Nordic Pulp & Paper Research Journal | Volume: | 29 | Número: | 2 | Local de edição ou do evento: | Sundsvall | Resumo: | The increase of filler content in paper without significantly sacrificing the paper mechanical resistances is of high interest for papermakers. In this work, precipitated calcium carbonate (PCC) modified with silica was used as filler for papermaking. Handsheets based on a eucalyptus kraft pulp furnish with different amounts of the modified filler, ranging from 16 to 40%, were produced. For similar levels of filler content it was found that the strength properties of the handsheets produced with the modified PCC were always significantly better than those obtained with the unmodified PCC. In particular, for handsheets with a filler content of 30%, the tensile index and the Scott bond internal resistance improved by ca. 20% and 39%, respectively. Some decrease of the light scattering and opacity values was noted when using the modified PCC, but the brightness was roughly the same, for each filler level evaluated. The enhanced fibre-to-filler bonding can be due to the hydrogen bonding between the cellulosic fibres and the hydroxyl groups of the silica film coating the calcium carbonate crystals, during the sheet formation. The present results with the new modified PCC provide a possibility to increase the filler amount in the papermaking industry. | URI: | https://hdl.handle.net/10316/28277 | ISSN: | 2000-0669 | DOI: | 10.3183/npprj-2014-29-02-p240-245 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Química - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
2014 - Paper NPPRJ 2014.pdf | 158.91 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
33
Visto em 15/abr/2024
Citações WEB OF SCIENCETM
28
Visto em 2/abr/2024
Visualizações de página
261
Visto em 23/abr/2024
Downloads 50
883
Visto em 23/abr/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.