Título: | Nanoindentation of functionally graded hybrid polymer/metal thin films | Autor: | Nunes, J. Piedade, A. P. |
Palavras-chave: | Functionally graded coating; Stents; Nanocomposite; Hybrid polymer/metal; Nanoindentation | Data: | 1-Nov-2013 | Editora: | Elsevier | Citação: | NUNES, J.; PIEDADE, A. P. - Nanoindentation of functionally graded hybrid polymer/metal thin films. "Applied Surface Science". ISSN 0169-4332. Vol. 284 (2013) p. 792-797 | Título da revista, periódico, livro ou evento: | Applied Surface Science | Volume: | 284 | Resumo: | Hybrid functionally graded coatings (2D-FGC) were deposited by magnetron co-sputtering from poly(tetrafluoroethylene) (PTFE) and AISI 316L stainless steel (316L) targets. The carbon and fluorine content varied from 7.3 to 23.7 at.% and from 0 to 57 at.%, respectively. The surface modification was developed to change the surface of 316L vascular stents in order to improve the biocompatibility of the outmost layer of the metallic biomaterial. In-depth XPS analysis revealed the presence of a graded chemical composition accompanied by the variation of the film structure. These results were complemented by those of transmission electron microscopy (TEM) analysis that highlighted the nanocomposite nature of the coatings. The nanomechanical characterization of 2D-FGC was performed by nanoindentation at several loads on the thin films deposited onto two different steel substrates: 316L and AISI M2. The study allowed establishing 0.7 mN as the load that characterized the coatings without substrate influence. Both hardness and Young modulus decrease with the increase of fluorine content due to the evolution in chemical composition, chemical bonds and structure. | URI: | https://hdl.handle.net/10316/27179 | ISSN: | 0169-4332 | DOI: | 10.1016/j.apsusc.2013.08.009 | Direitos: | openAccess |
Aparece nas coleções: | I&D CEMMPRE - Artigos em Revistas Internacionais FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Nanoindentation of functionally graded hybrid polymer metal thin films.pdf | 421.42 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
8
Visto em 29/abr/2024
Citações WEB OF SCIENCETM
10
6
Visto em 2/abr/2024
Visualizações de página
309
Visto em 30/abr/2024
Downloads
325
Visto em 30/abr/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.