Title: Quantification of Residual Stress Relief by Heat Treatments in Austenitic Cladded Layers
Authors: Rebelo Kornmeier, Joana
Marques, Maria José 
Gan, Weimin
Batista, António Castanhola 
Paddea, Sanjooram
Loureiro, Altino 
Keywords: residual stresses; neutron diffraction; contour method; stainless steel cladding; heat treatment
Issue Date: 12-Feb-2022
Project: UID/EMS/00285/2020 
Serial title, monograph or event: Materials
Volume: 15
Issue: 4
Abstract: The effect of the heat treatment on the residual stresses of welded cladded steel samples is analyzed in this study. The residual stresses across the plate's square sections were determined using complementary methods; applying diffraction with neutron radiation and mechanically using the contour method. The analysis of the large coarse grain austenitic cladded layers, at the feasibility limits of diffraction methods, was only made possible by applying both methods. The samples are composed of steel plates, coated on one of the faces with stainless steel filler metals, this coating process, usually known as cladding, was carried out by submerged arc welding. After cladding, the samples were submitted to two different heat treatments with dissimilar parameters: one at a temperature of 620 °C maintained for 1 h and, the second at 540 °C, for ten hours. There was some difference in residual stresses measured by the two techniques along the surface of the coating in the as-welded state, although they are similar at the welding interface and in the heat-affected zone. The results also show that there is a residual stress relaxation for both heat-treated samples. The heat treatment carried out at a higher temperature showed sometimes more than 50% reduction in the initial residual stress values and has the advantage of being less time consuming, giving it an industrial advantage and making it more viable economically.
URI: https://hdl.handle.net/10316/103377
ISSN: 1996-1944
DOI: 10.3390/ma15041364
Rights: openAccess
Appears in Collections:I&D CEMMPRE - Artigos em Revistas Internacionais
FCTUC Física - Artigos em Revistas Internacionais

Show full item record

SCOPUSTM   
Citations

5
checked on Oct 28, 2024

WEB OF SCIENCETM
Citations

4
checked on Oct 2, 2024

Page view(s)

101
checked on Oct 29, 2024

Download(s)

92
checked on Oct 29, 2024

Google ScholarTM

Check

Altmetric

Altmetric


This item is licensed under a Creative Commons License Creative Commons