Title: Estudo do fenómeno de relaxação de tensões na liga de alumínio 7050-T6
Other Titles: The mean relaxation phenomenon in 7050-T6 aluminum alloy
Authors: Branco, Mário Gabriel Ferreira 
Orientador: Costa, José Domingos Moreira da
Branco, Ricardo Nuno Madeira Soares
Keywords: Relaxação de tensões; Fadiga oligocíclica; Liga de alumínio 7050-T6; Circuitos de histerese; Rotura por fadiga; Mean relaxation; Low-cycle fatigue; 7050-T6 Aluminum alloy; Histereses loops; Fatigue failure
Issue Date: 27-Feb-2018
Serial title, monograph or event: Estudo do fenómeno de relaxação de tensões na liga de alumínio 7050-T6
Place of publication or event: Departamento de Engenharia Mecânica
Abstract: As ligas de alumínio da série 7000 são usadas num vasto número de aplicações estruturais, devido, principalmente, ao facto de combinarem elevada resistência específica, e boa resistência à corrosão. A liga 7050 é particularmente atrativa para a conceção de componentes aeronáuticos, o que se deve, de uma forma geral, às suas excelentes propriedades mecânicas, elevada resistência à corrosão, e boa tenacidade à fratura. Para além disso, a maioria destes componentes está sujeita a ciclos de tensão e deformação variáveis ao longo do tempo, o que os torna particularmente vulneráveis a falhas por fadiga. Nessa perspetiva, quer o desenvolvimento de novos componentes, quer a definição de intervalos de inspeção adequados, pressupõe a utilização de modelos de previsão de vida tão exatos quanto possível. Ora, o desenvolvimento de um modelo adequado pressupõe, em primeira instância, a utilização de propriedades de fadiga do material rigorosas. A presente tese tem como objectivo principal caraterizar o comportamento da liga de alumínio 7050-T6 no regime da fadiga oligocíclica, dando-se ênfase especial ao efeito da razão de deformação (Rε). Os ensaios são efetuados em controlo de deformação, para amplitudes de deformação (∆ε/2) entre 0.5% e 1.5%, considerando valores de Rε iguais a -1, 0 e 0.5. Após os ensaios, as superfícies de fratura são analisadas por microscopia eletrónica de varrimento, para identificar os principais mecanismos de fratura. .
Aluminum alloys of the 7000 series are used in a wide number of structural applications, mainly because they combine high specific strength and good corrosion resistance. The 7050 alloy is particularly attractive for the design of aeronautical components, which is generally due to its excellent mechanical properties, high corrosion resistance, and good fracture toughness. In addition, most of these components are subject to varying stress and strain cycles over time, which makes them particularly vulnerable to fatigue failure.In this perspective, both the development of new components and the definition of adequate inspection intervals presuppose the use of life expectancy models as accurate as possible. However, the development of an appropriate model presupposes, in first instance, the use of stringent fatigue properties of the material. The main objective of this thesis is to characterize the behavior of the 7050-T6 aluminum alloy in the regime of low-cycle fatigue, with special emphasis on the effect of the strain ratio (Rε). The tests are performed under strain-controlled conditions for strain amplitudes (Δε /2) between 0.5% and 1.5%, considering values of Rε equal to -1, 0 and 0.5. After the tests, the fracture surfaces are analyzed by scanning electron microscopy to identify the main fracture mechanisms. .
Description: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia
URI: http://hdl.handle.net/10316/86043
Rights: openAccess
Appears in Collections:UC - Dissertações de Mestrado

Files in This Item:
File Description SizeFormat
Dissertação_MIEM_2018_Mário Branco_2010126150.pdf3.08 MBAdobe PDFView/Open
Show full item record

Page view(s) 50

334
checked on Sep 14, 2020

Download(s) 50

333
checked on Sep 14, 2020

Google ScholarTM

Check


This item is licensed under a Creative Commons License Creative Commons