Título: | Electrochemical, morphological and microstructural characterization of carbon film resistor electrodes for application in electrochemical sensors | Autor: | Gouveia-Caridade, Carla Soares, David M. Liess, Hans-Dieter Brett, Christopher M. A. |
Palavras-chave: | Carbon film electrodes; Carbon film resistors; Cyclic voltammetry; Electrochemical impedance spectroscopy; Contact mode AFM; Confocal Raman spectroscopy; X-ray diffraction | Data: | 1-Set-2008 | Citação: | Applied Surface Science. In Press, Corrected Proof: | Resumo: | The electrochemical and microstructural properties of carbon film electrodes made from carbon film electrical resistors of 1.5, 15, 140 [Omega] and 2.0 k[Omega] nominal resistance have been investigated before and after electrochemical pre-treatment at +0.9 V vs SCE, in order to assess the potential use of these carbon film electrodes as electrochemical sensors and as substrates for sensors and biosensors. The results obtained are compared with those at electrodes made from previously investigated 2 [Omega] carbon film resistors. Cyclic voltammetry was performed in acetate buffer and phosphate buffer saline electrolytes and the kinetic parameters of the model redox system Fe(CN)63-/4- obtained. The 1.5 [Omega] resistor electrodes show the best properties for sensor development with wide potential windows, similar electrochemical behaviour to those of 2 [Omega] and close-to-reversible kinetic parameters after electrochemical pre-treatment. The 15 and 140 [Omega] resistor electrodes show wide potential windows although with slower kinetics, whereas the 2.0 k[Omega] resistor electrodes show poor cyclic voltammetric profiles even after pre-treatment. Electrochemical impedance spectroscopy related these findings to the interfacial properties of the electrodes. Microstructural and morphological studies were carried out using contact mode Atomic Force Microscopy (AFM), Confocal Raman spectroscopy and X-ray diffraction. AFM showed more homogeneity of the films with lower nominal resistances, related to better electrochemical characteristics. X-ray diffraction and Confocal Raman spectroscopy indicate the existence of a graphitic structure in the carbon films. | URI: | https://hdl.handle.net/10316/5022 | DOI: | 10.1016/j.apsusc.2008.03.180 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Química - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
file424dc205420d4b0e96e68b85cbff66fa.pdf | 1.63 MB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
14
Visto em 16/set/2024
Citações WEB OF SCIENCETM
14
Visto em 2/fev/2024
Visualizações de página 50
499
Visto em 10/set/2024
Downloads
354
Visto em 10/set/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.