Título: | Mechanical and surface analysis of Ti0.4Al0.6N/Mo multilayers | Autor: | Tavares, C. J. Rebouta, L. Andritschky, M. Guimarães, F. Cavaleiro, A. |
Palavras-chave: | Multilayers; Ultramicrohardness; Adhesion; Residual stress; Roughness | Data: | 2001 | Citação: | Vacuum. 60:3 (2001) 339-346 | Resumo: | The quest for hard materials that are able to sustain elevated stresses as tools or cutting processes has led to the investigation of (Ti,Al)N/Mo multilayer coatings. These structures have been deposited by dc magnetron sputtering on high-speed steel and stainless-steel substrates and designed with modulation periods of approximately 13 nm, up to a total thickness of 2.8 [mu]m. Experimental X-ray diffraction (XRD) achieved the basics involving structural quality and texture while RBS provided the composition. From AFM observations the waviness of the surface was monitored and it was found that the rms roughness values were minimised for a bias voltage of -120 V. Ultramicrohardness values of 33 GPa were obtained for the best samples, and their adhesion to the steel substrates was also studied. Residual stress measurements revealed a compressive stress state that prevailed in these structures, ranging from -0.2 to -1.3 GPa. | URI: | https://hdl.handle.net/10316/4294 | DOI: | 10.1016/s0042-207x(00)00413-9 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
filefa7616b83e694719b8edd42edf37f29f.pdf | 330.56 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
8
Visto em 15/abr/2024
Citações WEB OF SCIENCETM
7
Visto em 2/mai/2023
Visualizações de página 20
733
Visto em 23/abr/2024
Downloads 50
458
Visto em 23/abr/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.