Título: On the formation of intermetallic matrix composites produced by mechanical alloying and sputtering
Autor: Neves, F. 
Duarte, N. 
Trindade, B. 
Palavras-chave: Ti-Al intermetallics; Mechanical alloying; Vapor deposition; Powder metallurgy; Mechanical properties
Data: 2007
Citação: Journal of Alloys and Compounds. 434-435:(2007) 378-382
Resumo: (Ti-48Al)-based intermetallics were synthesized by a combination of mechanical alloying, sputtering and hot isostatic pressure techniques. Blended elemental powders of TiH2 and Al with nominal composition TiH2-48Al were mechanically alloyed for different periods of time. The powders were then coated with Ti and Ag and subsequently hot isostatically pressed at 900 °C with a maximum pressure of 150 MPa for 2 h. Finally they were heat treated at 1200 °C for 4 h. After processing, the compacts obtained from the TiH2-48Al coated powders had a lower hardness but a higher Young's modulus and fracture-toughness than the uncoated compacts. Therefore, the combined used of mechanical alloying, sputtering and compaction techniques might be an alternative method for the synthesis of compacts with non-conventional microstructures, formed by surface modified intermetallic particles.
URI: https://hdl.handle.net/10316/4203
DOI: 10.1016/j.jallcom.2006.08.281
Direitos: openAccess
Aparece nas coleções:FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato
filea6fefb4585884da9b5e5b878f30bbc2a.pdf953.42 kBAdobe PDFVer/Abrir
Mostrar registo em formato completo

Visualizações de página 50

470
Visto em 10/set/2024

Downloads

273
Visto em 10/set/2024

Google ScholarTM

Verificar

Altmetric

Altmetric


Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.