Title: On the formation of intermetallic matrix composites produced by mechanical alloying and sputtering
Authors: Neves, F. 
Duarte, N. 
Trindade, B. 
Keywords: Ti-Al intermetallics; Mechanical alloying; Vapor deposition; Powder metallurgy; Mechanical properties
Issue Date: 2007
Citation: Journal of Alloys and Compounds. 434-435:(2007) 378-382
Abstract: (Ti-48Al)-based intermetallics were synthesized by a combination of mechanical alloying, sputtering and hot isostatic pressure techniques. Blended elemental powders of TiH2 and Al with nominal composition TiH2-48Al were mechanically alloyed for different periods of time. The powders were then coated with Ti and Ag and subsequently hot isostatically pressed at 900 °C with a maximum pressure of 150 MPa for 2 h. Finally they were heat treated at 1200 °C for 4 h. After processing, the compacts obtained from the TiH2-48Al coated powders had a lower hardness but a higher Young's modulus and fracture-toughness than the uncoated compacts. Therefore, the combined used of mechanical alloying, sputtering and compaction techniques might be an alternative method for the synthesis of compacts with non-conventional microstructures, formed by surface modified intermetallic particles.
URI: http://hdl.handle.net/10316/4203
Rights: openAccess
Appears in Collections:FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat
filea6fefb4585884da9b5e5b878f30bbc2a.pdf953.42 kBAdobe PDFView/Open
Show full item record

Page view(s) 50

321
checked on Jun 1, 2020

Download(s)

89
checked on Jun 1, 2020

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.