Title: Estudo da sensibilidade de materiais compósitos à presença de gases redutores
Authors: Santos, Hugo André Rodrigues dos 
Orientador: Faia, Pedro Manuel Gens De Azevedo de Matos
Keywords: Compostos cerâmicos; Sensores
Issue Date: Jan-2013
Abstract: Os óxidos metálicos semicondutores são vulgarmente utilizados na produção de sensores de gases. Estes quando se encontram compactados na forma volúmica possuem estruturas porosas, que ao estarem expostas a diferentes atmosferas, e como resultado de reacções de adsorção/dessorção dos gases pelo sólido, podem dar origem à variação da sua condutância. Neste trabalho, produziram-se 2 amostras cerâmicas a partir da mistura de 88,75% de TiO2 com 11,25% de ZnO, sinterizadas a 500ºC. As amostras foram sujeitas para várias temperaturas, a diferentes concentrações de CO e, posteriormente, de humidade. Para se ficar a conhecer o comportamento dos sensores, no âmbito da sensibilidade e repetibilidade, foram adquiridos os valores da variação da sua resistência, medida através de um procedimento em corrente contínua. Os dados adquiridos foram posteriormente analisados. Tendo como preocupação a liberdade do utilizador, foi necessário melhorar a automatização do banco de ensaios já existente, tendo para tal foi sido desenvolvido software em ambiente labVIEW que permite o controlo das misturas dos gases, armazenamento dos resultados obtidos, monitorização do estado de funcionamento dos componentes do sistema e por fim a desativação do mesmo.
The metallic oxide semiconductors are commonly used in the production of gas sensors. When compacted, these semiconductors present porous structures, which when exposed to different atmospheres, as a result of adsorption/desorption reactions of gases by the solid, may originate the variation of their conductance. In the scope of this work, two ceramic samples were produced, in the proportions of 88.75% with 11.25% of TiO2 and ZnO respectively, and sintered at 500 ° C. Both samples were subjected at various temperatures to different concentrations of carbon monoxide and later to different humidity levels. In order to know the behavior of these sensors within the sensitivity and repeatability fields, the values of their resistance variation were obtained, using a direct current measuring. The acquired data was subsequently analyzed. Having the user freedom as a concern, improvements to the automation of the existent test bench were necessary. Therefore, software was developed in labVIEW environment, the new software tool developed allows the control of the gases mixture, the storage of the acquired data, the monitorisation of the system components and finally system shut down.
URI: http://hdl.handle.net/10316/41685
Rights: openAccess
Appears in Collections:FCTUC Eng.Electrotécnica - Teses de Mestrado

Files in This Item:
File Description SizeFormat 
Dissertação_HugoSantos_2013.pdf2.43 MBAdobe PDFView/Open
Show full item record

Page view(s)

64
checked on Jul 16, 2019

Download(s)

17
checked on Jul 16, 2019

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.