Title: | Caracterização e qualificação de partículas de óxidos metálicos, obtidos por detonação | Authors: | Ornelas, João Manuel Nunes | Orientador: | Campos, José Leandro Simões de Andrade | Keywords: | Detonação; Alumina; Magnesia; Titania Espinela Zirconia; Aplicações das nano partículas; Purificação; Detonation; Alumina; Magnesia; Titania Zirconia Spinel; Applications of nano particles; Purification | Issue Date: | 22-Sep-2014 | Place of publication or event: | Coimbra | Abstract: | O objectivo deste trabalho é a formação de nanoparticulas de óxidos metálicos
por detonação. Foram estudadas, como caso demonstrativo, a alumina, a magnesia, a
titania e a zirconia. Foram também estudadas duas espinelas de formação com base na
alumina. A previsão dos produtos da detonação foi efectuada com o programa THOR.
Na formação de partículas por detonação surgem impurezas,
fundamentalmente originadas pela grande concentração de carbono nos produtos da
detonação. Foi estudado, como caso demonstrativo, a purificação da zirconia com o
recurso à "lavagem” com uma solução aquosa de ácido nítrico. O melhor resultado foi
obtido com um tempo de permanência de vinte minutos. Este processo leva uma
desagregação das partículas com a consequente eliminação de grande parte dos resíduos de
carbono (detectável pela cor da solução aquosa de ácido nítrico). As amostras recolhidas
no teste de purificação foram analisadas ao microscópico óptico e electrónico SEM. para
uma caracterização granulométrica The objective of this work is the formation of nanoparticles of metal oxides detonation. Were investigated as demonstrative case, alumina, magnesia, titania and zirconia to. We also studied two spinels training based on alumina. The prediction of the detonation products was performed with the THOR program. In the formation of particles by detonation impurities, mainly caused by the high concentration of carbon in the detonation products arise. Purification of zirconia with the use of "washing" with an aqueous solution of nitric acid was studied as demonstrative case.'s Best result was obtained with a dwell time of twenty minutes. This process takes a breakdown of the particles with the consequent eliminating much waste of carbon (detectable by the color of the aqueous solution of nitric acid). samples collected during the purification test were analyzed by optical and electronic microscopy SEM. for texture characterization. |
Description: | Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra | URI: | https://hdl.handle.net/10316/39017 | Rights: | openAccess |
Appears in Collections: | UC - Dissertações de Mestrado FCTUC Eng.Mecânica - Teses de Mestrado |
Files in This Item:
File | Description | Size | Format | |
---|---|---|---|---|
Caracterizacao e qualificacao de particulas de oxidos metalicos obtidas por detonacao.pdf | 5.96 MB | Adobe PDF | View/Open |
Page view(s)
315
checked on Oct 15, 2024
Download(s) 20
1,312
checked on Oct 15, 2024
Google ScholarTM
Check
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.