Title: Structural and electrochemical characterization of Zr–C–N–Ag coatings deposited by DC dual magnetron sputtering
Authors: Velasco, S. Calderon 
Lopez, V. 
Alves, C .F. Almeida 
Cavaleiro, A. 
Carvalho, S. 
Keywords: A. Ceramic; A. Zirconium; A. Stainless steel; B. EIS; B. XRD; C. Anodic films
Issue Date: Mar-2014
Publisher: Elsevier
Citation: VELASCO, S. Calderon [et al.] - Structural and electrochemical characterization of Zr–C–N–Ag coatings deposited by DC dual magnetron sputtering. "Corrosion Science". ISSN 0010-938X. Vol. 80 (2014) p. 229-236
Serial title, monograph or event: Corrosion Science
Volume: 80
Abstract: ZrCN coatings with incorporated silver were deposited on 316L stainless steel by dual reactive magnetron sputtering to evaluate the silver influence on the structural properties and corrosion resistance of the films. Samples composition was assessed by electron probe microanalysis. Glow discharge optical emission spectroscopy was used to determine the distribution of silver in the films. Structural characterization was performed by X-ray diffraction and Raman spectroscopy. Corrosion resistance was evaluated by potentiodynamic test and electrochemical impedance spectroscopy. Results revealed enhanced corrosion resistance properties of the coated steel and higher coatings reactivity when incorporated with silver, showing a plausible silver release increment.
URI: http://hdl.handle.net/10316/27176
ISSN: 0010-938X
DOI: 10.1016/j.corsci.2013.11.036
Rights: openAccess
Appears in Collections:I&D CEMUC - Artigos em Revistas Internacionais
FCTUC Eng.Mecânica - Artigos em Revistas Internacionais

Show full item record

SCOPUSTM   
Citations

17
checked on Jun 25, 2019

WEB OF SCIENCETM
Citations

17
checked on Jun 25, 2019

Page view(s) 50

441
checked on Oct 16, 2019

Download(s)

104
checked on Oct 16, 2019

Google ScholarTM

Check

Altmetric

Dimensions


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.