Please use this identifier to cite or link to this item:
Title: The influence of paper surface sizing on inkjet pigment penetration
Authors: Costa, Tiago G. 
Gamelas, José A. 
Moutinho, Isabel M. 
Figueiredo, M. Margarida 
Ferreira, Paulo J. 
Keywords: Surface sizing; Ink pigment; Iimage analysis; Inkjet printing; Papel
Issue Date: Oct-2010
Publisher: Appita Journal
Serial title, monograph or event: Appita Journal
Volume: 63
Issue: 5
Abstract: The effect of paper surface sizing on inkjet pigment penetration was evaluated by studying four different paper samples: one taken as reference, without surface sizing (paper RP), one surface sized with cationic starch (RPS1), one with a mixture of cationic starch and poly(styrene-co-maleic anhydride) (RPS2), and one with a mixture of cationic starch and poly(styreneco- acrylate) (RPS3). Assessment was based on the grey level analysis of a black printed area on the top surface of the paper samples and on internal layers below that printed area (obtained by delamination of the paper sheets). From the grey level distribution curves it was possible to confirm that the majority of the ink was retained at the top surface, as expected. The penetration degree of the ink pigment was RPS1 < RPS3 << RPS2 << RP and the results were found to be related to the polar component of the surface energy. The ink penetration into the paper sheets was less pronounced for the papers with a higher surface polar character due to the stronger interactions between the water based ink and the surface sizing agents. The highest ink penetration was observed for sample RP due to the very low polarity (and lower topographical uniformity) of its surface.
ISSN: 1038-6807
DOI: 10.1080/1350178X.2014.939690
Rights: openAccess
Appears in Collections:FCTUC Eng.Química - Artigos em Revistas Internacionais

Files in This Item:
File Description SizeFormat
PJF - Appita - 2010.pdf955.52 kBAdobe PDFView/Open
Show full item record


checked on Jun 2, 2021

Page view(s) 20

checked on Jun 10, 2021


checked on Jun 10, 2021

Google ScholarTM




Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.