Título: | Effects of O addition on the thermal behaviour of hard W-N sputtered coatings | Autor: | Louro, C. Oliveira, J. C. Cavaleiro, A. |
Palavras-chave: | Tungsten oxynitride; Sputtering; Thermal behaviour; HT-XRD; Hardness | Data: | 16-Jun-2009 | Editora: | Elsevier Ltd. | Citação: | Vacuum. 83:10 (2009) 1224-1227 | Resumo: | The structural thermal behaviour of three W-O-N sputtered coatings with similar metalloid to metal ratio (~2.1) was investigated up to 900 °C after annealing in a vacuum tube furnace as well as in-situ HT-XRD under a controlled atmosphere of Ar-5%H2. The as-deposited microstructure of the coatings consisting in a nanocomposite of low-order W-O and W-N phases evaluated differently as a function of the oxygen content. The W-O-N film containing more than 27 at.% O delaminated severely from the steel substrates for temperatures as low as 500 °C. In opposite, for the coatings with less O content, the low range order of the as-deposited structure was maintained up to 800 °C and with further annealing crystallized into a mixture of WO2 and W2N. The thermal behaviour of the oxynitride films overcame that observed for oxygen-free nitride ones. This is due to the greater N content retaining during annealing treatment, in opposite to the W-N films which give rise to the single metallic [alpha]-W phase. The structural and compositional evolution supported the hardness behaviour obtained by the thermal treatment in protective ambiance | URI: | https://hdl.handle.net/10316/12888 | ISSN: | 0042-207X | DOI: | 10.1016/j.vacuum.2009.03.015 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
Effects of O addition on the thermal behaviour.pdf | 489.79 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
6
Visto em 7/out/2024
Citações WEB OF SCIENCETM
6
Visto em 2/out/2024
Visualizações de página 50
527
Visto em 15/out/2024
Downloads
339
Visto em 15/out/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.