Título: | Optimization of the sintering process of raw material wastes | Autor: | Vieira, M. T. Catarino, L. Oliveira, M. Sousa, J. Torralba, J. M. Cambronero, L. E. G. González-Mesones, F. L. Victoria, A. |
Palavras-chave: | Powder technology; Ceramics | Data: | 1999 | Citação: | Journal of Materials Processing Technology. 92-93:(1999) 97-101 | Resumo: | The analysis of the mineralogical composition of most rock wastes shows the presence of a high percentage of minerals with SiO2 and Al2O3, which could be used as raw materials for ceramic products. The main objective of this work is to recover wastes from one primary rock industry, utilised in the production of tiles and flooring, for the manufacturing of ceramics, using powder technology: pressing and sintering. The sinterability of the powders, with and without previous heat treatment, was studied in order to obtain a product with the best performance. Powders from different quarries after being uniaxial pressed at 40 MPa, or isostatic pressed at 170 MPa and sintered within the range 1150-1170°C present properties as follows: (a) hardness: 5.5-7.5 GPa; (b) transverse rupture strength: 55-94 MPa; (c) abrasion and erosion wear better than that of bulk to be drawn materials, and (d) water absorption of less than 0.5%. The results allow the conclusion that these wastes can be recovered and used successfully in the manufacture of ceramics with better performance than traditional tiles and flooring. | URI: | https://hdl.handle.net/10316/4313 | DOI: | 10.1016/S0924-0136(99)00186-7 | Direitos: | openAccess |
Aparece nas coleções: | FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
file2278c601b4ee45a8b1b4aff068e3a349.pdf | 402.85 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
34
Visto em 23/set/2024
Visualizações de página 50
474
Visto em 1/out/2024
Downloads 10
2.188
Visto em 1/out/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.