Title: Efeito do “micro-shot-peening” na propagação de fendas por fadiga na liga aeronáutica Al 7475-T7351
Other Titles: Effect of micro-shot-peening on fatigue crack propagation in Al 7475-T7351 aeronautical alloy
Authors: Mira, Gonçalo Miguel Beirão de 
Orientador: Ferreira, José António Martins
Antunes, Pedro Alexandre de Almeida do Vale
Keywords: Micro Shot Peening; Fadiga; Propagação de fenda; AL 7475-T7351; Microdureza; Microestrutura; Micro Shot Peening; Fatigue; Crack Growth; Al 7475-T7351; Micro-hardness; Microestructure
Issue Date: 20-Feb-2015
Place of publication or event: Coimbra
Abstract: Esta dissertação tem como objectivo mostrar a influência do tratamento superficial de Micro Shot Peening (MSP) na propagação de fenda por fadiga, na liga aeronáutica AL 7475-T7351. A análise é feita tendo em conta a influência da espessura dos provetes, a razão de carga utilizada nos ensaios de fadiga e o efeito retardante do bloco de sobrecarga na forma da fenda. De modo a compreender melhor o efeito do tratamento superficial de Micro Shot Peening na propagação de fenda, foram efectuadas medições de rugosidade de superfície, microdureza e microestrutura, tanto em provetes polidos, como em provetes tratados superficialmente pela técnica de MSP. Os resultados obtidos mostraram um pequeno aumento nos valores de microdureza, consequência das deformações plásticas impostas pelo tratamento. Todavia, devido à incorrecta optimização dos parâmetros de Micro Shot Peening, não sendo esta a mais adequada, tal fez-se sentir nos defeitos superficiais existentes nos provetes, o que, consequentemente, conduziu a uma redução de resistência à propagação de fenda.
The main objective of the work presented is to show the influence of the superficial treatment of Micro Shot Peening on the crack growth by fatigue in an aerospace alluminum alloy AL 7475-T7351. The analisys is done taking into account the specimen thickness, the charge ratio used in fatigue tests and the retardant effect of the overlad block in the shape of the crack. In order to understand better the performance of the crack growth, roughness, microhardness and microestruture tests were done, both in the polished and in the surface treated specimen. Results shown a small increase in the microhardness values, outcome of the plastic deformations imposed by the treatment. However, because of the bad optimization of the Micro Shot Peening parameters. Surface defects appeared, which consequently, led to a reduction of the crack growth resistance.
Description: Dissertação de Mestrado Integrado em Engenharia Mecânica apresentada à Faculdade de Ciências e Tecnologia da Universidade de Coimbra.
URI: https://hdl.handle.net/10316/39088
Rights: openAccess
Appears in Collections:UC - Dissertações de Mestrado
FCTUC Eng.Mecânica - Teses de Mestrado

Show full item record

Page view(s) 50

429
checked on Mar 26, 2024

Download(s) 50

535
checked on Mar 26, 2024

Google ScholarTM

Check


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.