Título: | Nanocrystalline Au:Ag:SnO2 films prepared by pulsed magnetron sputtering | Autor: | Reddy, A. Sivasankar Figueiredo, N. M. Cavaleiro, A. |
Palavras-chave: | A. Oxides; A. Thin films; C. X-ray diffraction | Data: | Jun-2013 | Editora: | Elsevier | Citação: | REDDY, A. Sivasankar; FIGUEIREDO, N. M.; CAVALEIRO, A. - Nanocrystalline Au:Ag:SnO2 films prepared by pulsed magnetron sputtering. "Journal of Physics and Chemistry of Solids". ISSN 0022-3697. Vol. 74 Nº. 6 (2013) p. 825-829 | Título da revista, periódico, livro ou evento: | Journal of Physics and Chemistry of Solids | Volume: | 74 | Número: | 6 | Resumo: | Influence of annealing temperature on structural, compositional, surface morphology, electrical, and optical properties of pulsed magnetron sputtered nanocrystalline Au:Ag:SnO2 films was investigated by several analytical techniques. From the XRD results, the films were polycrystalline with the absence of impurity phases and the films were grown preferentially in the (110) orientation of SnO2 with tetragonal structure. The surface smoothness and grain size of the films increases with annealing temperature. Photoluminescence measurements show that the as deposited Au:Ag:SnO2 films exhibited a broad emission peak at 536 nm (2.31 eV). The lowest electrical resistivity of 0.005 Ω cm was obtained at the films annealed at 500 °C. The optical studies show that the visible transmittance and band gap of the films increases with annealing temperature. | URI: | https://hdl.handle.net/10316/27181 | ISSN: | 0022-3697 | DOI: | 10.1016/j.jpcs.2013.01.023 | Direitos: | openAccess |
Aparece nas coleções: | I&D CEMMPRE - Artigos em Revistas Internacionais FCTUC Eng.Mecânica - Artigos em Revistas Internacionais |
Ficheiros deste registo:
Ficheiro | Descrição | Tamanho | Formato | |
---|---|---|---|---|
pulsed magnetron sputtering.pdf | 648.64 kB | Adobe PDF | Ver/Abrir |
Citações SCOPUSTM
13
Visto em 25/mar/2024
Citações WEB OF SCIENCETM
5
12
Visto em 2/mar/2024
Visualizações de página 50
397
Visto em 26/mar/2024
Downloads 50
359
Visto em 26/mar/2024
Google ScholarTM
Verificar
Altmetric
Altmetric
Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.